注射成型(阻燃ABS)ABS AF366F 韩国LG
观看注射成型(阻燃ABS)ABS AF366F 韩国LG视频:
ABS AF366F 韩国LG
熔体质量流动速率 | 220°C/10.0kg | ASTMD1238 | 70 | g/10min |
收缩率 | MD:3.20mm | ASTMD955 | 0.40到0.70 | % |
拉伸模量3 | 3.20mm | ASTMD638 | 2160 | Mpa |
抗张强度4 | 屈服,3.20mm | ASTMD638 | 39.2 | Mpa |
伸长率4 | 屈服,3.20mm | ASTMD638 | 5.0 | % |
断裂,3.20mm | ASTMD638 | >20 | % | |
弯曲模量5 | 6.40mm | ASTMD790 | 2350 | Mpa |
弯曲强度5 | 6.40mm | ASTMD790 | 65.7 | Mpa |
热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 89.0 | °C |
1.8MPa,未退火,6.40mm | ASTMD648 | 83.0 | °C | |
维卡软化温度 | ASTMD15256 | 90.0 | °C | |
RTIElec | UL746 | 60.0 | °C | |
RTIImp | UL746 | 60.0 | °C | |
RTI | UL746 | 60.0 | °C | |
-30°C,3.20mm | ASTMD256 | 59 | J/m | |
-30°C,6.40mm | ASTMD256 | 49 | J/m | |
23°C,3.20mm | ASTMD256 | 210 | J/m | |
23°C,6.40mm | ASTMD256 | 160 | J/m | |
洛氏硬度 | R级 | ASTMD785 | 105 | |
UL阻燃等级 | 1.5mm | UL94 | V-0 | |
2.0mm | UL94 | V-05VB | ||
2.5mm | UL94 | V-05VA | ||
3.0mm | UL94 | V-05VA |