ABS AS1003FR BK-038-5 SABIC沙伯创新
观看ABS AS1003FR BK-038-5 SABIC沙伯创新视频:
ABS AS1003FR BK-038-5物性表
收缩率 | MD:24小时 | ISO294-4 | 0.27 | % |
吸水率 | 24hr,50%RH | ASTMD570 | 0.20 | % |
收缩率 | MD:24小时 | ASTMD955 | 0.30 | % |
TD:24hr | ASTMD955 | 0.40 | % | |
TD:24小时 | ISO294-4 | 0.39 | % | |
拉伸模量2 | ASTMD638 | 3160 | Mpa | |
拉伸模量 | ISO527-2/1 | 2700 | Mpa | |
抗张强度 | 屈服 | ASTMD638 | 42.1 | Mpa |
拉伸应力 | 屈服 | ISO527-2 | 38.0 | Mpa |
抗张强度 | 断裂 | ASTMD638 | 39.3 | Mpa |
拉伸应力 | 断裂 | ISO527-2 | 37.0 | Mpa |
伸长率 | 屈服 | ASTMD638 | 2.6 | % |
拉伸应变 | 屈服 | ISO527-2 | 2.2 | % |
伸长率 | 断裂 | ASTMD638 | 6.2 | % |
拉伸应变 | 断裂 | ISO527-2 | 2.8 | % |
弯曲模量 | ASTMD790 | 3050 | Mpa | |
ISO178 | 2800 | Mpa | ||
弯曲强度 | ASTMD790 | 75.8 | Mpa | |
弯曲应力 | ISO178 | 66.0 | Mpa | |
热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 96.7 | °C |
热变形温度4 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 93.0 | °C |
热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 88.3 | °C |
热变形温度4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 78.0 | °C |
线形热膨胀系数 | MD:-40到40°C | ASTME831 | 7.7E-05 | cm/cm/°C |
MD:-40到40°C | ISO11359-2 | 7.1E-05 | cm/cm/°C | |
TD:-40到40°C | ASTME831 | 6.3E-05 | cm/cm/°C | |
TD:-40到40°C | ISO11359-2 | 9.3E-05 | cm/cm/°C | |
表面电阻率 | ASTMD257 | 10to1.0E+3 | ohms | |
体积电阻率 | ASTMD257 | 1E+04 | ohms·cm | |
ShieldingEffectiveness | 3.00mm | 内部方法 | 50to65 | dB |
悬壁梁缺口冲击强度3 | 23°C | ISO180/1A | 7.0 | kJ/m² |
装有测量仪表的落镖冲击 | 23°C,EnergyatPeakLoad | ASTMD3763 | 15.0 | J |
UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 18 | kJ/m² |
23°C | ASTMD4812 | 310 | J/m | |
23°C | ASTMD256 | 53 | J/m |