PPO/PA基础创新塑料(泰国)GTX9400W-1710物性表
| 熔融指数 | ASTM D1238 | 97 | g/10min | |
| 模压收缩率 | flow,3.2mm | GE Method | 1.2-1.4 | % |
| 拉伸应力 | 屈服 | ASTM D638 | 65 | Mpa |
| 断裂 | ASTM D638 | 62 | Mpa | |
| 拉伸模量 | 50mm/min | ASTM D638 | 1960 | Mpa |
| 弯曲应力 | ASTM D790 | 101 | Mpa | |
| 弯曲模量 | ASTM D790 | 2360 | Mpa | |
| 拉伸应力 | 50mm/min | ISO 527 | 69 | Mpa |
| 弯曲模量 | 2mm/min | ISO 178 | 2710 | Mpa |
| IZOD冲击强度 | 无缺口，23℃ | ASTM D4812 | 849 | J/m |
| 无缺口，-30℃ | ASTM D4812 | 769 | J/m | |
| 缺口，23℃ | ASTM D256 | 256 | J/m | |
| 缺口，-30℃ | ASTM D256 | 112 | J/m | |
| 维卡软化温度 | ASTM D1525 | 212 | °C | |
| 热变形温度 | 0.45MPa,3.2mm | ASTM D648 | 191 | °C |
| 1.84MPa,3.2mm | ASTM D648 | 84 | °C | |
| 0.45MPa,6.4mm | ASTM D648 | 203 | °C | |
| 1.82MPa,6.4mm | ASTM D648 | 170 | °C | |
| 维卡软化温度 | ISO 306 | 203 | °C | |
| 熔化温度 | 270-295 | °C | ||
| 干燥温度 | 95-105 | °C | ||
| 干燥时间 | 3-4 | h |
其他新闻
- 原料包装图PPO/PA GTX914-14101 基础创新塑料(欧盟) 2024-04-29
- PPO/PA国产料 VP7139-701 基础创新塑料(上海) 2024-04-29
- PPO/PA GTX600-7001耐水解 基础创新塑料(日本) 2024-04-29
- 隔壁产地PPO/PA 基础创新塑料(日本) GTX918WR-7001 2024-04-29
- PPO/PA 日本旭化成 AT600 2024-04-29
- 代理(尼龙+PPO)PPO/PA 日本旭化成 A0210 2024-04-29
- PPO/PA 日本三菱工程 NXG7100N（华南塑胶市场库房库存） 2024-04-29
- PPO/PA 日本三菱工程 C61HL BLACK 2024-04-29
- 工厂库存PPO/PA C82HL GRAY 日本三菱工程 2024-04-29
- 牌号物性免费PPO/PA 日本三菱工程 NX7000N 2024-04-29
- 出售原包PPO/PA 日本三菱工程 BX505 2024-04-29
- 全系列进口牌号齐全PPO/PA基础创新塑料(美国) 2024-04-29
- 尽请了解PPO/PA GTX9400W-1710 基础创新塑料(美国) 2024-04-29
- 本厂从事PPO/PA CRN500 基础创新塑料(美国) 2024-04-29
- PPO/PA华南工厂直销PPO/PA基础创新塑料(美国)GTX679 2024-04-29
联系方式
- 地址：广东省东莞市樟木头镇百果洞新城街三巷11号101室（注册地址）
- 邮编：523622
- 电话：0769-89070333
- 销售部经理：吴海群
- 手机：13686289316
- 传真：0769-89070333
- QQ：782215440
- Email：qunfasj@163.com
产品分类
站内搜索