ABS BDT5510-1000 沙伯基础CYCOLAC原厂原包料
![](http://static.11467.com/img/ab-prev-0.png)
![](http://shop.11467.com/2022/06-22/2617932011_small.jpg)
![](http://shop.11467.com/2022/06-22/2617932011_small.jpg)
![](http://shop.11467.com/2022/06-04/3792626321_small.jpg)
![](http://img.11467.com/2022/06-05/1676576377_small.jpg)
![](http://img.11467.com/2022/06-21/2840470235_small.jpg)
![](http://img.11467.com/2022/08-09/2409555445_small.jpg)
![](http://static.11467.com/img/ab-next-0.png)
更新时间:2024-07-03 10:11:00
价格:请来电询价
品牌:基础创新塑料(美国)
特性:低光泽
名称:ABS
联系电话:0769-89070333
联系手机:13686289316
联系人:吴海群
让卖家联系我
详细介绍
ABS BDT5510-1000 沙伯基础CYCOLAC原厂原包料
ABS BDT5510-1000 沙伯基础CYCOLAC原厂原包料
熔体粘度 | 260°C,1000sec^-1 | ASTMD3835 | 163 | Pa·s |
密度 / 比重 | ASTMD792 | 1.05 | g/cm³ | |
熔体质量流动速率 | 230°C/3.8kg | ASTMD1238 | 6.0 | g/10min |
220°C/10.0kg | ISO1133 | 14 | g/10min | |
SpiralFlow2,3 | 内部方法 | 73.7 | CM | |
收缩率 | MD:3.20mm | 内部方法 | 0.50to0.80 | % |
拉伸模量4 | ASTMD638 | 2280 | Mpa | |
拉伸模量 | ISO527-2/1 | 2930 | Mpa | |
抗张强度6 | 屈服 | ASTMD638 | 53.0 | Mpa |
拉伸应力 | 屈服 | ISO527-2/50 | 43.0 | Mpa |
弯曲模量7 | 50.0mm跨距 | ASTMD790 | 2460 | Mpa |
ISO178 | 2030 | Mpa | ||
弯曲强度7,8 | ISO178 | 67.0 | Mpa | |
弯曲强度7 | 屈服,50.0mm跨距 | ASTMD790 | 81.0 | Mpa |
Gardner光泽度 | 60°,无织构 | ASTMD523 | 25 | |
热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 92.0 | °C |
热变形温度11 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 95.0 | °C |
热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 81.0 | °C |
热变形温度11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 83.0 | °C |
维卡软化温度 | ISO306/B50 | 98.0 | °C | |
线形热膨胀系数 | MD:-40到60°C | ASTME831 | 1.4E-04 | cm/cm/°C |
简支梁缺口冲击强度9 | -30°C | ISO179/1eA | 7.2 | kJ/m² |
23°C | ISO179/1eA | 13 | kJ/m² | |
悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 290 | J/m |
悬壁梁缺口冲击强度10 | -30°C | ISO180/1A | 7.0 | kJ/m² |
23°C | ISO180/1A | 13 | kJ/m² | |
落锤冲击 | 23°C | ASTMD3029 | 35.0 | J |
UL阻燃等级 | 1.5mm | UL94 | HB |
相关产品
联系方式
- 地址:广东省东莞市樟木头镇百果洞新城街三巷11号101室(注册地址)
- 邮编:523622
- 电话:0769-89070333
- 销售部经理:吴海群
- 手机:13686289316
- 传真:0769-89070333
- QQ:782215440
- Email:qunfasj@163.com
产品分类
站内搜索